Fortron 1342L4 PPS Ticona
Fortron 1342L4 PPS Ticona
Fortron 4184L4 PPS Ticona
Fortron 4184L6 PPS Ticona
Fortron 4332D4 PPS Ticona
Fortron 1342L4 PPS Ticona 材料物性表如下:
Physical | Nominal Value | Unit | Test Method |
Specific Gravity | |||
-- | 1.70 | g/cm3 | ASTM D792 |
-- | 1.69 | g/cm3 | ISO 1183 |
Molding Shrinkage | |||
Flow | 0.20 to 0.30 | % | ASTM D955 |
Across Flow | 0.50 to 0.70 | % | ASTM D955 |
Across Flow | 0.50 | % | ISO 294-4 |
Flow | 0.20 | % | ISO 294-4 |
Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 14400 | MPa | ISO 527-2/1A/1 |
Tensile Strength | |||
Break, 23°C | 152 | MPa | ASTM D638 |
Break | 165 | MPa | ISO 527-2/1A/5 |
Tensile Elongation | |||
Break, 23°C | 2.0 | % | ASTM D638 |
Break | 1.6 | % | ISO 527-2/1A/5 |
Flexural Modulus (23°C) | 13700 | MPa | ISO 178 |
Flexural Strength 3 | 245 | MPa | ISO 178 |
Coefficient of Friction | |||
vs. Steel - Dynamic 4 | 0.16 | ASTM D1894 | |
vs. Steel - Static | 0.20 | ISO 8295 | |
vs. Steel - Static 4 | 0.20 | ASTM D1894 | |
vs. Unknown - Dynamic 5 | 0.21 | ASTM D1894 | |
vs. Unknown - Dynamic 6 | 0.28 | ASTM D1894 | |
vs. Unknown - Static 6 | 0.31 | ASTM D1894 | |
vs. Unknown - Static 5 | 0.27 | ASTM D1894 | |
Wear Factor 7 | ASTM D3702 | ||
416 Stainless: 32°C | 166 | 10^-10 in3·min/ft·lb·hr | |
C-1018 Steel: 49°C | 323 | 10^-10 in3·min/ft·lb·hr | |
C-1018 Steel: 93°C | 825 | 10^-10 in3·min/ft·lb·hr |
Fortron 0205 PPS Ticona
Fortron 1120L4 PPS Ticona
Fortron 1130L0 PPS Ticona
Fortron 1130L4 PPS Ticona
:鄧
:86-
傳真號(hào)碼:86-
地址:中國(guó) 廣東 東莞 東莞市 樟木頭鎮(zhèn) 塑膠原料市場(chǎng)
Fortron 1342L4 PPS Ticona玻纖40%其它產(chǎn)品
Fortron 1342L4 PPS Ticona玻纖40%
Fortron 1200L1 PPS Ticona高粘度
Fortron 1141L4 PPS Ticona玻纖40%
Fortron 1140LC6 PPS Ticona玻纖40%
Fortron 1140L7 PPS Ticona耐化學(xué)性
Fortron 1140L6 PPS Ticona玻纖40%
Fortron 1130L4 PPS Ticona玻纖30%
Fortron 1130L0 PPS Ticona玻纖30%
Fortron 1120L4 PPS Ticona玻纖20%
Fortron 0205 PPS Ticona熱穩(wěn)定